CV Data Analysis through OriginLab - Calculation of Specific Capacitance - 17

[@abdulhaseebhatti]

Sir sir sir sir, wallah it's brilliant... You have no idea how much you helped me

[@RahulKumar-wx6jz]

Hi man, I have seen all of yr videos. Really helped me in research. Please upload more. Thanks.

[@ananyasagnihotri7333]

Thank you! Found it very useful. Please upload a tutorial on calculating surface area, heterogeneous rate constant from the Laviron equation using CV data.

[@muthiahpillaipalanichamy3939]

Excellent presentation. Thanks to you

[@nanoworld6122]

Glad it was helpful!

[@rilujoseph9591]

Excellent Video! So useful!!!!!!

[@Mosesnewtechnology]

Thank you for that great and easy-to-follow procedure, it's very helpful

[@amrradwan4279]

Excellent video, go ahead!

[@shadeepa]

Many thanks for uploading. very helpful video

[@RAVIKUMAR39496]

So great Sir. You have strong teaching skill. Your way of presentation can very nice sir thank you so much

[@dingzhang3588]

could you please show how to calculate electrochemical active surface area (ECSa)

[@dr.alial-riyahee1202]

Thank you so much dear. I am still waiting additional videos of Cyclic Voltammetry.

[@treewhite596]

Thank you for the content, really useful.

[@prg2457]

fantastic job, very informative.

[@nanoworld6122]

Glad you enjoyed it!

[@sumitdubal7887]

Thank you. Nice explanation. Please share some videos related Galvonastatic charge discharge test with calculation of energy density and power density.

[@ZaidLHadi]

Fantastic ... it's a good idea .. keep going ...thanks a lot

[@maedeharvani4124]

A perfect explanation! Thank you.

[@nanoworld6122]

Glad you enjoyed it!

[@adithya4993]

Great content!!!! Finding it helpful!!!!

[@AbdulWahab-ub6kt]

Really helpful and significant video. Thanks a lot for uploading such great work. Dear Team Nanoworld! Would you please attach reference of paper describing this method. It’ll further add authenticity to calculations illistrated in this video. Regards.

[@randomthoughts8782]

ur video is nice but i am facing problem that current at y=axis is in 10exp-7 range and mostly in vidos and reported data it is in 10exp-4 range as is in ur case, m i doing mistake in some conversion or what? please guide

[@kevinkantize844]

very very helpful, well detailed, i loved it. Thank you so much.

[@shakrajabeen9522]

Thankyou so much for sharing.....

[@BiplabKDeka]

Great explanation. really helpful. Plz make videos on how to calculate Energy and power density with unit conversion.

[@aliyaliyah4759]

this is really helpful! thank you for explain this

[@AsmaaHamdyTamam]

really appreciate your efforts. Could I ask how could you calculate the specific capacitance from three electrode system in GCD and CV. thanks in advance

[@nilankardiyali8121]

Sir, what will be the unit of area calculated from the CV curve?

[@SMS-yq8ks]

Thanks a lot. It is very useful

[@EnglishSimplified27]

pls tell what is unit of I current

[@rana2585]

please add a video on overpotential calculation from CV nd LSV... also for onset potential

[@farhanzafar9030]

Amazing work

[@nanoworld6122]

Thank you! Cheers!

[@meme1usa]

I loved this video, thank you so much!!!

[@nanoworld6122]

Glad you enjoyed it!

[@공희정-r1h]

Thank you. It is very helpful.

[@manzarch2700]

very informative👍

[@IftikharAnfal]

I wish the music was not that dominant

[@le5722]

Thank you for the nice video! When calculate the enclosed area, what is the difference between the function of Polygon-absolute area and Integrate-absolute area?

[@zubairahmad2538]

Thanks for nice video. Could you show how to calculate Capacitance from charge and discharge curves .

[@uthmanalli4636]

Looking forward to this. especially when you have a battery like discharge curve. Thanks

[@renukakumari8064]

Good evening sir..How can I get specific capacity from cyclic voltametery curve?

[@aadilkhan9196]

A.O.A Really good one and nicely explained.But I have an objection. I hope you will try to resolve it. During surface area calculation we should use area within the CV loop , actually you divide the equation by 2 to get that area (area within the CV loop) .But in example solution you have determined that area (within the loop) then you should not divide the equatiuon by 2.

[@nanoworld6122]

This formula is used for both, i.e. 2 electrodes as well as 3 electrodes electrochemical work station data. In the case of the 2 electrode system, if we considered the electrodes are symmetric (ideally) then we should not divide it by 2 ( we considered it is already divided). I performed my CV characterization in 3 electrodes electrochemical work station ( As I mention it in my video), that's why I divide it by 2.

[@randomthoughts8782]

@@nanoworld6122 i am facing problem that current at y=axis is in 10exp-7 range and mostly in vidos and reported data it is in 10exp-4 range as is in ur case, m i doing mistake in some conversion or what? please guide

[@sharafpc786]

What does the capacitance during discharge exactly means? Little confused here.. isn't it the device capacitance? Why need to subtract it from charging capacitance to get the device capacitance?

[@ranaarslanafzal4452]

Can you help me with the Electrochemical active surface area calculation?

[@collegephysics3362]

Nice video

[@TheIITianleader]

please make a video of detailed calculation of galvanostatic Charge discharge for a Supercapacitor.

[@Cutepie-tg1re]

kzbin.info/www/bejne/nIOlloR5hdx2gtE

[@Tsastm]

Sir what is the interpretation of the area of the CV curve? I mean if it's large what does it say and vice-versa

[@ruchindagooneratne7684]

Love all the vids! I do have a question with regard to the final equation. Since the absolute area was used, shouldn't eq (6) be used instead of (10)? Meaning, that the specific capacitance doesnt need to be divided by 2? Thanks!

[@muhammadadeelasghar3236]

Good observation. I've explained it in my comment.

[@troi818]

@@muhammadadeelasghar3236 Can you explain agian why you did not use equation 6 since the area from origin is already absolute area?

[@kirannargatti]

Really helpful and great explanation. But one thing is not clear, in case of 3 electrode system if we consider absolute area from origin software, then the capacitance equation will be A/2mk(v2-v1) or A/mk(v2-v1)? and in given example, final answer 33.89 is correct or it should be 67.78?

[@mdsaifurrahman5376]

Thanks for sharing

[@9847356129]

calculate diffusive and capacitive contributions for electrode material can you do video on this

[@SiddhantB9]

Very helpful video, thanks a lot. I had a question which I hope you'll help me with. Why is the area A2 = (V1 - V2) Cp*m*k at 6:36?

[@nanoworld6122]

This was for discharching of capacitor.

[@randomthoughts8782]

ur video is nice but i am facing problem that current at y=axis is in 10exp-7 range and mostly in vidos and reported data it is in 10exp-4 range as is in ur case, m i doing mistake in some conversion or what? please guide

[@usamahmahmood1099]

very helpful thanx

[@sabashahin_]

how to find area under a curve with respect to y-axis on Origin?

[@ahmedattia7941]

hank you for the nice video! When calculate the enclosed area, what is the difference between the function of Polygon-absolute area and Integrate-absolute area?

[@uthmanalli4636]

Can we get an answer to this question, please? I've been curious about it. They both give different values of area, and I've seen different videos where integrate-absolute area has been used instead of polygon-absolute area, Why is this?

[@sharafpc786]

Yes please

[@zahraa3maran]

How I can get the file pdf , please.

[@mohamedbousnobra7989]

Merci bien pour la video. Quel est l'intervalle de Cp qui permet de juger que le matériau étudié peut être utilisé dans le stokage des énergies? Est il possible d'avoir le contenu de cette video sour forme de fichier word ou pdf

[@jagadeswarchandra4951]

the integration has an error , the v in k is not included

[@Oceancoop]

Thanks for nice video.

[@nanoworld6122]

Always welcome

[@mennatullahghaleb5916]

Thanks alot

[@guadalupesuarez5002]

I have a doubt, the potential is in Volts not mV such as appear in the original file? and the rate scan in mV?

[@nanoworld6122]

yes, the potential is in Volts and the scan rate in in mV

[@randomthoughts8782]

ur video is nice but i am facing problem that current at y=axis is in 10exp-7 range and mostly in vidos and reported data it is in 10exp-4 range as is in ur case, m i doing mistake in some conversion or what? please guide

[@randomthoughts8782]

in origin file, potential is in mv range

[@raghvendradubey3228]

Hi, excellent tutorial...👏 could you please elaborate, how to prepare solution and electrodes configuration during electromica?l process

[@nanoworld6122]

Will upload soon

[@MuhammadZiaurrehmanFaurooqi]

Mashallah great

[@navinmech540]

How A2 is just negative of A1? A2 magnitude is lesser than A1.

[@ManSingh-mw1il]

i have one query. you have area in (AV), mass in (g), scan rate in (mV/s), potential window in (V) so how do you got capacitance in F/g. I think area should be in (mAV)

[@nanoworld6122]

Please re-watch this video, and note everything in your note book and then re-think about it.

[@ManSingh-mw1il]

@@nanoworld6122 yes sir, i got it now, you have converted scan rate into V/s during calculation. Thank you for replying sir.

[@adillasasongko7227]

Why it divided by two?

[@yhana8836]

Hi, I have a question. How ti know the mass of active material

[@nanoworld6122]

Hello Mulya, You can measure it through weight balance.

[@mouhcineazriouil4544]

@@nanoworld6122 I think the masse used in the preparation of concentration which the CV recorded in.

[@speedstar6140]

Don't you think that the unit of scan rate should also be V/s instead of mV/s that you are using while calculating Cp in excel sheet. Since 1 F is equal to 1 A.s/V

[@nanoworld6122]

I think you did not watch it carefully. When putting formula, I multiply it with 10^-3. This means I already used V/s for the rate. Please re-watch

[@speedstar6140]

@@nanoworld6122 Ok

[@subalakshmi3835]

thank you

[@nanoworld6122]

You're welcome

[@shashikantyadav1473]

Hi Sir, Can you please provide that CV data excel file. I just want to plot and calculate the area for discharging time? If possible please help me with charging and discharging formula on the basis of C&V. Thanks and regards,

[@wildamardhatillah5784]

「ビデオサウンドは、私の想像を超えて、かなり良いです」、

[@chemistrybangladesh]

nice

[@shelkaze6242]

thanks for tutorial, much helpful.lol

[@NareshKumarD17]

could you please share this word file

[@nanoworld6122]

Please send me an email asking for the file.

[@zahraa3maran]

@@nanoworld6122 your email,please 🙏

[@mohammadmansour5299]

Please i need this word document quickly😢

[@kusuma33]

alhamdulillah.....

[@renukakumari8064]

Please reply sir 🙏

[@loverspptloversppt1480]

you need to clarify the content

[@uchechichibukomiracle1958]

Thank you

[@nanoworld6122]

You're welcome

[@novmannabeel8080]

thank you