3D Print to Solid Metal, BETTER Than Lost PLA Casting

[@PaulsGarage]

Zamak12 available at rotometals.com Want me to personally teach you how to use your 3d printer to make whatever you want in metal? Click here: paulsmakeracademy.mykajabi.com/joinus

[@FrancescaMazur]

The ducting you showed was single wall HVAC pipe. That garbage offgasses when heated, and if you're not in a well ventilated area, you can develop heavy metal poisoning. You should have a disclaimer in there. Great video though, gonna try this.

[@stevrgrs]

Yeah it’s like the idiots recommending torching galvanized steel for “the pretty colors” it makes 🤦‍♂️

[@stevenbradley6572]

I honestly can't think of many things that don't release gasses or harmful fumes when heated, especially with a torch. Most people won't drink out of a plastic bottle if it sat in the sun for 5 minutes. At this point it is common knowledge.

[@MAcDaTHo]

@@stevenbradley6572 Zinc has a special place in toxin heaven... It is not comparable to the "toxins" you get from a plastic bottle. Plus: This also happens to people who know the danger. So no, THIS is NOT common knowledge. (I have the feeling you live in a world, where everything is toxic)

[@87elky383able]

Pro tip…no vacuum chamber? a counter top foodsaver or equivalent with the hose attatchment for sealer jars👍

[@beefan1596]

This is a genius idea. I don't want to break the bank on equipment, but investment casting seems to be the way to go for me. If this method works, then you just saved me a lot of money. Now all I have to do is find a way to obtain a burnout oven for cheap :P

[@ChaosPootato]

This feels like therapy or something... A Paul video with no spilling, stuff works, result looks great, Paul is happy... very nice

[@PaulsGarage]

I definitely tried to screw that skull up but sometimes things just work lol

[@evren.builds]

The ducts might be and are probably galvanized. Be mindful that heat will cause the zinc coating to vaporize. When zinc vaporizes, it can create zinc oxide fumes. Great tips love your content

[@PaulsGarage]

Yes they are galvanized. Fortunately everything is already well ventilated for the plastic that's burning out and the propane 👍

[@FFA704]

@@PaulsGarage Bad answer, heavy metal poisoning wont make you sick or dizzy it will permanently ruin your life

[@FFA704]

@@PaulsGarage Good video nonetheless

[@mmccubbis3662]

That’s all I could think about when I saw that part. Zinc oxide is potent fatal. I did like the video otherwise 😊

[@TrogdorBurnin8or]

You're focused on the micron-thin layer of zinc on the ducts, which never gets especially hot in the first place, rather than the hundreds of grams of molten ZAMAK, which is 96% zinc.

[@MikelNaUsaCom]

so... building a lathe out of Za-12?

[@PaulsGarage]

I am indeed yes

[@DEtchells]

I thought the question was a joke, but … cool! (A Gingery type thing or something more modern?)

[@PaulsGarage]

@@DEtchells modified gingery lathe

[@dekurvajo]

The only problem with Zamak, aside of relatively low melting point, that its kind of brittle material. In comparison, nylon is much stronger and actually sometimes even PLA is a better choice over Zamak.

[@dennisyoung4631]

Many parts will work well done in Za12.

[@TopHatBurgers]

Can't wait to see the "right way" to do it, bc I have a vacuum chamber, and perforated flasks. Great stuff, always enjoy your videos! Keep it up!

[@PaulsGarage]

I'm a couple pieces of equipment away from that but it's coming eventually👍

[@woodndrum303]

Claim - this stuff works, well wow it really does. I’m new here and this is a breath of fresh air! Good clear advice or info delivered at a fast pace and good shots of casts that are just fab. Like it a lot, thanks Paul.

[@PaulsGarage]

Thanks!

[@NeoIsrafil]

Polycast is great, the tip about prepainting with plaster is genius, especially for people without a vacuum chamber, so yah I concur, good advice here. I would suggest making sure you only use that vent tube outside only cuz it will poison you otherwise, and if you want higher resolution resin printing with burnout resin works the same as pla printing with burnout PLA but at a much higher rez. Couldn't have given better advice myself.

[@LunarburnStudio]

Polycast is definitely a solid step up from PLA, been using it for a couple of years now. It works great for small scale casting but gets a little squirrely when casting larger prints in ceramic shell. Good video, dig your channel.

[@PaulsGarage]

Good to know about the larger prints, thanks!

[@privateprivate3767]

what infill do you print Polycast for burn out? 80% 20%?

[@PaulsGarage]

I usually go as low as possible, 10-20% for most prints and I made no adjustments for polycast

[@privateprivate3767]

@@PaulsGarage thanx, you are really cool, I didn't even know this stuff existed

[@LunarburnStudio]

@@privateprivate3767 @paulsGarage The amount of infill for me depends on the size of the print. smaller prints are closer to 20% larger print (over 12" high) ill drop to 10%. The other variable is whether the print /object is a solid vs a thin walled hollow. Less for a sold, more for hollow. Ideally the less material you need to burn out the better.

[@travislawson1185]

This one video got a thumbs up and a subscribe from me. Thank you for this. I own a small business specializing in restoration of vintage automotive related hobbies such as racing karts, motorcycles and specialty cars and trucks. I am a professional fabricator and often times I have to methodically recreate broken or worn out parts that can not be purchased at any price. I have been seriously considering purchasing a decent 3d printer just for this purpose of assisting in sand casting and slurry casting of one off parts. Everything you said is music to the ears. Thank you again.

[@PaulsGarage]

That sounds awesome! That's why I got into metal casting, i wanted to make car parts. I got a bit distracted with 3d printing and fell way down the metal casting rabbit hole while my car project just sits there haha! This video isn't the ideal way to do it, actually. For plaster investment casting, I would use jewelry wax for sprues, and a vacuum casting machine. Any big car parts should probably be sand cast, but things like metal radio knobs, door handles, hood ornaments could be resin printed for better quality. I've always wanted to make a custom set of cylinder heads or intake manifolds or something, but that's a "one day when I get to it" kind of project, you know? 3d printers and 3d modeling is a great way to get patterns for casting. I would add 3d scanning to that, too. It's not the scale you're talking about, but I scanned a power wheels toy mustang and printed a full new body for it to look like greased lightning (video sometime in the future), so you're in good company here! I will say though with sand casting, it's vital you get the gating right to avoid porosity and sand and junk in your metal castings. Good luck and let me know what you're making!

[@travislawson1185]

@@PaulsGarage I currently have a small part for a vintage racing kart that I'm trying to recreate. It is a small carburetor intake reed valve body that was originally probably die cast aluminum. The part has a rather complex shape as it holds either 4 of 6 metal or fiberglass reeds and stands about 2 inches tall by about 2 inches round at the base. Material wise there is maybe 4-5 oz of aluminum. Originally this part cost $6-$10 in 1966 when it was developed. If you can even find one today that is good usable part, expect to pay north of $100. I know of at least 20 other restorer's actively looking for multiple parts for current projects. Even if I made them in batches of 20 or more at a time, I bet they would sell out quick. I would like to utilize the 3d print to cast method for short runs of parts like this before I dump thousands into a cnc made billet steel die and a pressure casting rig for a $40 part.

[@theblindbuildergrandminuti5648]

I used to do lost wax casting for Jewelry at a college and I wanted to get back into it for a long time. Thank you so much for this video. I just found your channel. Really looking forward to using Zamack Ingots and experimenting with all that, can’t wait to start making stuff!

[@PaulsGarage]

That's great! You can join the discord and share it with us if you want. Another good channel to look at is @vogman

[@amosbackstrom5366]

When I was like 14 I met a retired dentist in my neighborhood who had a whole jewelry casting workshop in his backyard. He taught me how to do lost wax casting and nickel and gold plating. One of the best memories of my childhood, I stopped playing videogames and football for a few months I went to his house almost every afternoon

[@PaulsGarage]

That sounds like an amazing opportunity. I wish more people would get that opportunity!

[@kaasmeester5903]

For jewelers who want to cast small parts with fine details, a resin printer may be a better option. There is a resin equivalent of polycast that has (casting) properties very similar to wax, and a lot of jewelers have started to use this.

[@sweetnightmere]

you can add silica sand or the red material like on the tennis court in the plaster for better resilience to heat and it doesn't crack as much when you do the burnout. 50/50 proportion sand and plaster

[@AlexanderGee]

As you sort of mentioned if you do lost PLA you absolutely have to use natural PLA with no colorants.

[@PaulsGarage]

Good point, I think as little junk in there to leave ash the better

[@RadarLeon]

I still like the idea of making a silicon mold using the pla print, casting in wax or simular other materials then casting a master mold by heating and melting the wax

[@GeordieT]

My preferred method. It also gives you the option to tidy up and smooth those print lines on the wax model before the final cast. If I'm making multiples then I'll silicon mould from the improved wax model. Personally, this is the necessarily long route through the woods I have to take because I'm not a sculptor and rely on the printer to do the hard work. Not sure I'll rush to use Zanak... I think the fumes issue outweighs the convenience for me.

[@jtjames79]

Use PVA, it's water soluble filament. Skip a step.

[@igoraugusto4629]

I recently thought of molds made with PVA, as it is water soluble, but with PVB it makes more sense mainly because it is easier to print, PVA ends up getting moisture very easily, which makes printing difficult, maybe HIPS would be an option , since it is soluble in delimonene. For those who still prefer PLA, Esun has PLA High flow, perhaps because of its ease of melting, it helps in the lost casting process.

[@josuelservin]

KZbin did that crap of just not showing me your videos on my subscriptions as if I had unsubscribed... Anyway, glad to have your videos back.

[@PaulsGarage]

Yeah they do that lol it happens to us all

[@Night_Hawk_475]

Fantastic video :o So many little gems of knowledge in here I'm not doing metal casting, and don't expect to be any time soon.... mayyybe some day - But that bit about painting some plaster onto the original print before making a mold of it, that's absolute genius. I've seen numerous casting videos before, and that's something /none/ of them have ever done - they've all either just accepted the bubbled pitting, or done crazy vacuum setups (and still accepted lesser pitting anyways)

[@extraziadeh]

Apparently the algorithm has blessed me today by recommending this video. Very cool and interested to try your tips. Thanks!

[@PaulsGarage]

The algorithm has been very kind to me lately

[@lundgrenbronzestudios]

I've just gotten into Lost PLA, I started using Ovature Black PLA and using an air compressor to blow it the mold after burn out and Its been working really well. I'm going to look into poly cast filament though. word to the wise though, those galvanized stove pipe will burn up and oxidize way too fast, you are better off getting a cut off of square tubing or steel pipe. stainless steel if possible.

[@PaulsGarage]

Air compressor is the only way I've heard of people successfully cleaning a PLA burnout, but I'm worried some molds might not get clean enough with that. No idea though, never tried. And good call about the thicker steel. These pipes don't look too good after use but the temps weren't as high as if I was doing bronze. Eventually I want to do vacuum casting so beefier flasks are totally a must

[@klausbrinck2137]

Aside to the great content, I find you are also very funny, the narration is a joy when someone´s so funny !!!

[@ProtonFilms_Mark]

I've been looking into ways of 3D printing a steering knuckle for my kid's Go Kart. It's got suspension, big wheels and a top speed of just 40kph, so I think it won't hurt giving Zamak a try for that purpose.

[@matthewellisor5835]

US cent coins since 1982 are 2.5% Copper and balance Zinc. Add in about 10-12% Aluminum and you're in range. Don't break any laws.

[@jerrysanchez5453]

Honestly glad I found this channel.its a no bullshit channel so far.pretty neat

[@johnmccanntruth]

Great info. You had me on the edge of my seat waiting for a big bed pour…

[@PaulsGarage]

So about that lathe bed... I have the pattern, I made those big flasks and then (dramatic pause) I realized I didn't have enough casting sand lol. I ordered more and the box just came in yesterday 👍

[@parcore2925]

I love this channel. It reminds me of the RedGreen show, but I learn some real, actual, good tips. Thanks!

[@PaulsGarage]

One day I hope to live up to the example set by red green 🤣

[@frikkiesmit327]

Glad i got your video..its something new in this way you shared. And im actually planning on casting something in a lost pla method. I will use pla as its what i have. 😅

[@JohnHansknecht]

Really cool! I'm starting to lean toward plating pla though. Recent videos show that if you paint it with a conductive graphite paint, it can be plated with nickel, and then other metals like gold on top of the nickel.

[@PaulsGarage]

That plating stuff is really awesome. It looks great in my opinion, but the end result is different. I'd rather have a piece that's solid metal, with all the weight, but not everybody is like me.

[@anthonyleggio4877]

I recently saw a video of testing different methods of getting a chrome finish on a part and the winner was this chrome nail polish stuff

[@klausbrinck2137]

still: 1st plate with copper, then with nickel. Nickel-plating directly isn´t easy...

[@defenestrated23]

What an info dump! I got tips for printing, glueing, smoothing, casting, and marital advice!

[@PaulsGarage]

Just remember I'm not legally liable if you end up divorced 🤣 my advice *might not* be great

[@anystrap404]

LOL, your comment on John Snow was fantastic! Great advice that I will remember as I start putting together my foundry setup. =]

[@nickitoff9629]

Dang! I know what I'm dong now! Awesome stuff, thanks for sharing. Your videos are great and your a great entertainer!

[@MrDiagorasofmelos]

Since PVB is dissolved by alcohol, and since plaster does not dissolve alcohol, could we consider clearing the PVB from the plaster in an ethanol bath?

[@FranklyWry]

Not dead yet! I must not have been the only one to comment on your slapdash (haven’t seen that word in a while, I bet) methods. Anyway, fun stuff, ya crazy guy.

[@ABaumstumpf]

It is always nice to see people discovering decade-old technology when looking to improve their new found technologies. Zamak is cheap-ish (not much cheaper than the alternatives anymore), easy to handle, relatively strong. Of course it also has its downsides - it is extremely susceptible to contaminations. Ever touched lead with the tongs you use to pick the Zamak? You just contaminated your zamak and it might rot away with just a few years. And while it is strong it loses strength with time and lacks some of the nice-to-have properties other materials have. Aluminium i significantly lighter and corrosion-resistant, iron (yes way harder to melt) is stronger and cheaper, copper has higher electric and thermal conductivity while also being more pliable etc. But for pure decorative parts casting Zamak is great.

[@dennisyoung4631]

Another idea for burnout containers is sections of Exhaust Pipe, especially stainless exhaust pipe.

[@stevenstafford1502]

Ive done this before with polysmooth! Works so well.

[@NM-wd7kx]

How is polysmooth to print with?

[@stevenstafford1502]

@@NM-wd7kx If its dry, it prints a lot like PLA but doesnt bridge as well. If its wet? Youre in for a bad time.

[@Londrino]

I've used MoldLay before with great results. It's the same price as polycast, but it's a wax filament that's easy to print with and melts out of the mold super easily.

[@hotrodderrecycler3202]

Very few coffee brans still use steel for there containers. Chuck Full O'Nuts is one brand.

[@wilsonmatos6734]

Please make a complete beginning guide to casting after you do it in ideal conditions. I'm looking to build a casting area in the shop... No idea the full scope of things.

[@PaulsGarage]

Good idea! That's quite an undertaking, id have to separate it up into sand casting, investment casting, etc... Most people don't do all of it. I've never done ceramic shell casting or vacuum casting for example. But it's a good idea to get it all in one place. That would be a super long video though haha

[@wilsonmatos6734]

@@PaulsGarage that's super fair. I am currently figuring out the melting of metal. I have no idea what a crucible is or where to get/make it. Kiln vs. forge vs. oven etc. I will research it once I have a solid project to execute, but this is so niche... The basics are often over looked and everyone kinda starts at step two, and assumes we know step 0 and 1. Like can I build a ceramic kiln that can melt steel... It seems like it should be possible... But does anyone actually do it? Why not?

[@iphoneawesome123]

I don't know if you're in that world at all, but I wonder how this could be used for the 3D2A world. Zamak used to be used in a lot of mass produced Saturday night specials back into he day. With PLA+ already being plenty strong, zamak could be that next step, especially for some frames that need the barrel pinned directly to it.

[@PaulsGarage]

No idea what 3D2A even is but if PLA can do it, zamak probably can too

[@iphoneawesome123]

@@PaulsGarage printing firearms and firearms accessories

[@PaulsGarage]

Ah ok that's pretty cool. I'm more of an archery guy personally 🏹

[@Preyhawk81]

some HiPoints are made from Zamac except the barrel.@@iphoneawesome123

[@lordnathan1]

I hope it could work. There is models id wanna do and aluminum and zamak would be my go to metals

[@NeoIsrafil]

If you want another tip, they make burnout resins too for lost RESIN casting from a 3d printer. They cost like 50 bucks a kilo, but they are WORTH IT. The quality is 100 times better than any fdm printer you own.. my fiance and i are doing our wedding rings using it to make a really pretty set of custom rings.

[@FeralMoonDesigns]

Really glad I watched this before I went out to buy the aluminum I was going to get to throw at someone. Now I'll be sure to get Zamak instead 😂

[@PaulsGarage]

Nothing worse than inadequate throwing metals 🤣

[@FeralMoonDesigns]

@@PaulsGarage If I'm going to do a job, I should do it right!

[@gordoncouger9648]

Finally, a Lost Wax casting process using 3D printed patterns that will make parts that work for real-world machines. Hi Point makes their firearms out Zmac ZA-12

[@SporadicUploads1]

Notes on the ZA alloy casting, it is toxic and can make you sick if you get the zinc oxide dusty vapors, also ZA27 is mechanically tough like for cutting or drilling, much harder to drill through than mild steel, its just zinc and aluminum.

[@Preyhawk81]

zink alloys melt under 500C if you dont heat to 900C you are fine

[@thedazzlingape2006]

another/better alternative to cast your investment into: instead of steel investment tubes, try PVC pipe or drainage segments, cut them to shape and give them a cut right down the center from end to end, tape the cut up and put your casting blank on a piece of tape and tape it to seal the bottom. after the plaster has become dry-wet, untape it and work the center split to release the whole mould from the PVC and then without waiting or using another tube, you can just keep going making more moulds from one piece of tube. and best of all, you never have to "clean out the plaster" when I started I did this simply using the caps of my tiny torch refill cans. so any flexible straight piece of tube plastick will work. maybe you dnt even need to spend a dime!

[@SuperSeaguard]

You can also smooth the polycast with a Polysher or just plain Isopropyl alcohol

[@70galaxie]

duct tape commercial grade makes a permanent seal. no breakdown or oxydiizing. everywhere that carries a large selection only has cheep stuff or has one small size of one fair/good type at a very high price

[@gendragongfly]

This is great 😃I've looked for easily castable (low temperature) alloys before, but didn't find much worth having. Zamak looks like it's pretty much perfect for most applications, unless weight is really an issue. Zamak 5 is known in the EU as Z410 and has mechanical properties close to 6061 aluminium. By weight it's cheaper but by volume it's around the same price as aluminium (at least from the suppliers that I have access to). Thanks for the great video 😊

[@patrickchristie82]

All I can say as thank you! Off to design custom truck emblems!

[@PaulsGarage]

Go for it!

[@skyrider4789]

Looking forward to the future “ideal” way. Thanks!

[@PaulsGarage]

I'll give you a sneak peak, every part except the burnout material and metal alloy is different 😉

[@scatdawg1]

Man this is a great video filled with non-stop useful information thank you for your service 🙏

[@PaulsGarage]

Thanks! Glad to ramble non stop, extra glad it's useful!

[@fernandoandaluz2281]

Thanks for the whole walkthrough bro, now I know. Legit

[@rossk7927]

I'm immediately curious if you can blue (nope) or anodize (yup, but don't yet know how practice it is to do at home) zamak, or how well it takes a powder coat or what paints will bond the best for a part ment to be handled... I'll dig around, just sharing the thoughts your video prompted 😊

[@coulterjb22]

Love Zamak. Looking forward to the next vid!

[@Festivaljunkie]

could one say cast a frame for a quadcopter that could be finished in a cnc or a jig/drill press?

[@PaulsGarage]

Probably yes. Lots of those kinds of parts are cast, though they tend to be die cast for production purposes. You would probably want aluminum though to save weight and that doesn't flow as nicely into details, but you can get around that in a couple ways

[@wardogdauwdd3020]

Can you do a video on melting zamek or zinc in a lead hotpot useing plaster for a mold

[@tannerortmann4187]

Thanks for the video! I never comment on videos but you seem like a decent guy so I wanted to say please, please don't melt zinc alloys in steel/iron alloy containers. Molten zinc acts like a solvent on iron alloys and will dissolve them. You'll lift your soup can from your foundry and have 4lbs of 1,000*F liquid dump out of the bottom. Also, since the steel is dissolved into the alloy, you can have weird pockets of rust develop over time which isn't really a problem for decorative things like you made in the video but if you were to make something structural or for outdoor use it would lead to pockets, bubbles, and weaknesses that you won't know are there until it breaks apart. I truly didn't mean to rant, zamak alloys are a life saver for detail work. There are several engine parts that can be great sources of cheap zamak also, carbs and throttle bodies in particular. Thanks again and good luck!

[@sierraecho884]

Here is a nother tip if you want to use aluminium. Use the right kind. There are casting alloys and wrought alloys. Casting alloy is found in hard drives fro example. It flows a lot better since it´s optimized for this task.

[@PaulsGarage]

Very true. I'm skipping the scrap step entirely from now on for casting that I want to be good. Buying certified ingots. I'm not giving up my scrap stash just yet though...

[@sierraecho884]

@@PaulsGarage Well you could bring your crap to a scrap yard and get some money for it which you can use to buy proper aluminium instead but of course this is entirely up to you. Just saying it is a possibility.

[@CPT_IDOL]

LOL! I am a single guy… And that is rule number one for buying a sofa… Always make sure you can lay down on it, and always make sure it’s comfortable enough to sleep on! 👍🏼😎👍🏼

[@TonyZXT]

Can you give a quick and dirty guestimate of what it would cost, equipment wise to do this on the cheaper end, but not so cheap I'd end up buying better equipment soon after? No need to take the time break it down, just in the ballpark is fine. Assuming all I already have is a printer. TIA, Great info!

[@PaulsGarage]

Hard to put an exact number on it but at minimum you need something to burn out the mold and something to melt the metal. One foundry furnace set up from an Amazon seller like vevor might work as long as you keep temperatures low, but a devil forge would be a step up. You could use the furnace for both like I did here. Plaster, filament, and the steel vents/soup cans etc... Are expendable, though, so prices go up the more you do it. Ideally you would have a small electric furnace to melt the metal and a small burnout oven, but prices go up considerably

[@JohnDoe-rx3vn]

Thanks for the heads up on the Zinc alloy, i was going to play with Aluminum Bronze but damn does it have a high melting point

[@PaulsGarage]

Aluminum bronze is pretty awesome for sure, but this is super easy

[@joshmellon390]

I use this lightweight PLA for printing RC airplane stuff. Well, it basically prints out styrofoam, and I wonder if it would work for burning out molds.

[@PaulsGarage]

Not sure. That stuff expands a lot right? I would be worried about it expanding too much and cracking the mold. Do you print the 3D lab print stuff? I have a few of those models, they are really cool

[@blacktridentgoods]

My buddy uses a wax based resin in his resin printer. Casts beautifully

[@PaulsGarage]

a resin printer is definitely on my list. The resolution is amazing

[@AgentPothead]

Foil tape is a little more annoying to use than duct tape. Understatement of the year? It's an early year so maybe. Great videos too, glad the algorithm lead me here.

[@maarkaus48]

Black pipe works too and you can get different sizes for it. Less nickle coating on it.

[@PaulsGarage]

Hey that's a good idea. Black pipe is tougher too

[@maarkaus48]

@@PaulsGarage Thank you. Its from experience. My mom was a silversmith/goldsmith and we did lots of casting together. we used black pipe (large,) with jeweler casting. We used a terrifying centrifuge to fire the molten gold/silver into the material at an impossibly high speed. I don't recommend that to the casual user as you can spray molten gold everywhere. Exciting? Yes, but not safe.

[@PaulsGarage]

@@maarkaus48 I've seen those things and I'm definitely going to pass on that! I'm going to build/buy/something a vacuum casting set up though

[@cryd1239]

I too have that 15 year old t-shirt. What a show.

[@PaulsGarage]

It was really good. It's the only time I saw something on Broadway.

[@idontwantcorporateretaliat6301]

There's a reason we use wax in "lost wax method". Printing in wax is a pain but back in college we'd dissolve grocery bags in the wax to harden its solid form to prep bronze molds. Point being, try polyethylene filament (grocery bags) and that may be the next best material to wax. Should be inexpensive.

[@aryez91]

Could you elaborate on this? Link to filament?

[@SV_Try_Magic]

That stuff is super expensive and Ive used it several times. I started just using the cheapest clear stuff I could find and making the walls and supports as minimal as possible.

[@spudnickuk]

Thank you for showing,I do have a quest, could you Try Esun Emate low Temp PCL filament for casting, as you can melt it at 65C but would love to know if it would be any good. as it prints pefectly with no layer lines.

[@PaulsGarage]

Great suggestion! I've never heard of that filament. Ive used esun black pla and its great for the price.

[@spudnickuk]

@@PaulsGarage I love Esun Products, and to say Mainly I use the PLA + for tools I hope to have a go at casting using Esun Emate low temp as much cheaper than Polycast

[@sammaldonado5931]

You just saved my poor mexican ass, where I just can't get good ceramic plaster and resin prints lol. love u man

[@PaulsGarage]

Glad I could help!

[@PatrickHoodDaniel]

Brilliant!!

[@thaddeusrobinson6866]

I feel obliged to echo what others have said: ZINC RELEASES DEADLY FUMES WHEN HEATED! DO NOT CAST OR FORGE ANYTHING WITH ZINC INDOORS!

[@truegret7778]

Is the math correct? I usually find good-great PLA from $16-22USD for 1Kg spools, where this PolyCast (from your link in the description) is $50USD for 750g spools ($66.66USD / Kg). Regardless, that looks like pretty good filament to use. The triceratops bust looks fantastic.

[@TheUpl8te]

I love the couch comment! I’ve told people for years that a comfortable couch and working 24s was the secret to a long happy marriage.

[@hansedrachensohn530]

Just adding some fine sand to the plaster will keep it from cracking and causing the flashing you had.

[@insight477]

When you melt down the Zamak ZA 12 does it burn off any elements or can you still reuse with ease?

[@PaulsGarage]

I've reused the metal a whole bunch of times, no issues. Za12 should only be zinc and aluminum, and i barely heat it up to liquid. Zinc has the reputation for boiling off because brass (copper alloyed with zinc) melts at a temperature *above* zincs boiling point. Keep it barely liquid and it shouldn't boil off at all, certainly not enough to screw up the alloy. Especailly with Za12, because zinc and aluminum aren't very sensitive as an alloy. you can basically have no aluminum or lots of aluminum and everything in the middle is ok, as long as you keep any and all lead as far away as possible.

[@gregorychaney7604]

That triceratops skull came out Great! For ornamental applications, it's hard to beat Zamak. I don't know if you need more gadgets, those castings would have been almost impossible using sand casting. Any thoughts about using a pouring basin and tapered sprue setup ? Have you picked up the zinc package yet? I wonder how it did in mail. Heavy for its size, not sure if cardboard was up to the task. Cheers from Alaska

[@PaulsGarage]

Hi Gregory! I did indeed pick up the package yesterday! I think I'll open it on a Livestream. I use a pouring basin and tapered sprue for sand casting, and I know VOGman does for investment prints, it's a good idea for sure.

[@gregorychaney7604]

Cool. Let me know when the livestream happens.

[@davib8963]

I bought a lot of PVB spools recently to experiment with. One thought was to try a silicone mold over a print, then dissolving the internal form with isopropyl over a month or so through a channel of some kind- I imagine it will not be quick. Could be totally bone headed, though i'd like to try it.

[@PaulsGarage]

You never know until you try it out!

[@eelcohoogendoorn8044]

I did try various experiments of this form; for parts that are hollow it will work decent; but if you have solidly printed detail bits with a high length/width ratio it can take very long. Also, how well this dissolving works strongly depends on temperature (and also moisture; do not use wet alcohol). Ive kept it in a slow cooker under the boiling point with good results, it cast with some really nice detail using zamak.

[@Kaimelar8]

Would a water soluble PVA also work for this technique?

[@twentystarseven]

Love your videos but I’m apparently extremely lazy. I bought some pvb minutes after watching this video. I placed my print directly into my molding sand and burned it out. Then poured a perfect casting with silver. You should try it.

[@medienmond]

Isnt PVB alcohol solluable? Why not use alcohol instead of burning the part out?

[@PaulsGarage]

great question. Yes PVB is alcohol solluable, but that could screw with the plaster, too. This plaster isn't ideal, but even something like prestige optima (the plaster I use now) shouldn't be dunked in liquid. The burnout process i just as much melting out the plastic as it is "firing" the plaster mold (think firing pottery- drying it out but also sintering particles together). This changes if you try using something like "suspend-a-slurry" ceramic shell. I dont' know if that can handle alcohol, but it can definitely be dunked in water before firing. I know some sculptors who boil those molds to get the wax out (so they can re-use it) but even then, they have to fire the ceramic shell anyway before casting. If you want to cast metal from a 3D print and you don't want to fire the mold, I would suggest sand casting instead. You can't make that triceratops head, but you can do a LOT with sand casting.

[@Calamity-Spice]

Zamak is called Mazak in the UK.

[@Bartspar68]

Hey Paul,, 7 min's in and I hit the subscribe button,, I like your style and your explinations..

[@PaulsGarage]

Thanks!

[@howardosborne8647]

Thanks for this really useful info on the Polycast filament and the Zamak alloys. Just the stuff I need for some steam engine castings👍

[@PaulsGarage]

Sounds good! Zamak is a bearing alloy too I think, it should work better than aluminum

[@dougsbir]

can you melt that metal on the hob or in an electric tandoor oven?

[@PaulsGarage]

No, it needs a bit higher temperature. Closer to 500c/900f to cast it

[@BUZZKILLJRJR]

Zamak is what high point uses on their slides for thier guns. I don't know ow the specific zamak allow they use I just k ow that's what they call it. If you can use it on gun parts you know it's strong enough stuff

[@mrtokyo9648]

Bro I love this video!

[@mrmollusk7367]

Are burnout resins expensive because they are more expensive to produce, or is it just not as in demand?

[@PaulsGarage]

For resins I'm not sure, but this filament is probably more expensive because it's a niche product, so volumes are lower, there are no fillers that would benefit the printing process because those might leave ash, and there is higher quality control. At least that's what the marketing says. Who knows if its true lol it does work though

[@AlwaysCensored-xp1be]

Yet another reason to try Zinc alloys. Always wanted to do white metal model trains. This plastic and Zamak might be better. I found white metal a little soft.

[@HeliosFire9ll]

How does this process compare to resin prints and lost wax casting? Could you make rings, etc from this technique?

[@PaulsGarage]

The burnout and casting process is exactly the same. Whatever you can print with polycast filament (or castable resin), you can cast in metal. Layer lines come through though, so beware of that. Polycast smooths with alcohol (IPA) which helps. I have some more recent videos with lost resin casting, all using plaster, but FDM prints might be better with ceramic shell casting, since that works better for larger prints. Not saying you can't use plaster, but the plaster can get expensive in large quantities

[@joshuadelisle]

Brilliant thanks 👍. Cheers J

[@PaulsGarage]

My pleasure!

[@qoohenqoo]

Would bronze and silver work with this same method?

[@PaulsGarage]

Yes! I've heard silver has some issues with detail but this is indeed how jewelers do it

[@eror151]

Would this process work with silver or metals that have to get to a higher temperature?

[@lordnathan1]

I'm sure it would. The highest metal you could melt with a at home smelter is aluminum, gold, silver, copper, brass, maybe cast iron if it's a good one.

[@jirvin4505]

Looking forward to your further experiments with Polycast. Like to see how it smooths out with pla

[@mattiasfagerlund]

If you only had one furnace, could you burn out the plastic then fill the mold with shot (small pieces of the casting metal) and let it melt inside the mold, or would that not work?

[@PaulsGarage]

That might work, not sure though.

[@rdr6253]

Great tips. Well done

[@GoingtoHecq]

Okay. I am interested in pvb. I will love to smooth it. I can finally "3d print an engine"

[@MakerGrigio]

Fantastic video, thank you so much!

[@PaulsGarage]

Thank for watching!

[@leoneventicinque6731]

What type of metal casting alloy is the best for mortar pestle, which must be adequately hard and heavy?

[@PaulsGarage]

Not sure I'd go with metal for that. The reason stone is used is because the hardness of silica is way above most other things including metal. I don't think I'd want to risk metal bits in food. Some metal can be toxic. Rocks bits (sand), other than being sharp, are chemically inert.

[@ARVash]

Could you just spray on a few coats of plaster and then burn out?

[@PaulsGarage]

The plaster needs to be in a block like that for strength. Ceramic shell uses just a coating but it's a lot stronger and reinforced with sand. Similar idea though

[@Scrap2Cast]

Hey Paul! Been a sub for a long time and I gotta say, love your vids brother! Thanks for sharing the info in this video. Definitely going to try your method! 🙂👊🏼👍🏼🍻

[@PaulsGarage]

Thanks and good luck!

[@Scrap2Cast]

@@PaulsGarage thanks, I’ll definitely need it!