The best way to teach MiG welding. Descending

The best way to teach MiG welding. Descending

[@davidtj91]

For those that don't know, this is not mig its FCAW (FLUX CORE ARC WELDING) they have the same semiautomatic process but this one is dual process with gas shielded and flux shielded.

[@Ben-tr]

is one better than the other?

[@smokerise]

@@Ben-tr flux core is stronger, but flux is usually ran uphill...solid wire can be very strong welds also, basically it depends on the experience of the hand holding the lead. In our shop it's a no no to run flux downhill...don't know why this guy is doing it. Solid wire can make nice downhill welds.

[@Ben-tr]

@@smokerise ty for the response

[@smokerise]

@@Ben-tr 👍

[@bloodybillanderson9294]

@@smokerise downhill welds are weaker at least thats what i was taught when welding on railroad equipment

[@bogdanmarkovic]

Arc retreating into the nozzle is a sign of slow wire speed. Also, you hold the torch too close to the workpiece. You just get a ton of slag onto the nozzle and you don’t get any significant gas coverage.

[@bogdan.1721]

esti sudor?

[@chrisinkansas1362]

Plus it's a downhill weld. Weakest of welds

[@jeffhanson9821]

@@chrisinkansas1362 downhand

[@BadarseBreakout]

It's flux core no gas so he doesn't need to be close for sure

[@smokerise]

@@chrisinkansas1362

[@josephlatourette8329]

With MIG welding you don't usually need to use a chipping hammer to get the slag off The shield gas usually stops that from forming which tells me that is flux core welding

[@natas0733]

Its dual shield

[@chrisplayz253]

I love the way he chipped the slag like it was going to reveal the greatest weld ever laid 😂😂😂

[@nucks4life11]

So how does mig have slag after the weld? Im a mig welder and there is no slag that needs chipping at all. Your heading/title should say something like flux core weld. .

[@smkyg]

maybe he is confused between flux cored and mig

[@nucks4life11]

@@smkyg yep

[@jaimelopez3229]

Looks like FCAW not mig...mig is hard wire no flux

[@travissawatzky9924]

If you're weaving on a CWB test plate in Canada the inspector will fail you on the spot unless it's a cap. Stringers are standard procedure just about everywhere.

[@samdigman9623]

What test spesificly? I wanna look up the test details and parameters.

[@danielbeaird6264]

​@Sam Digman It's not because of parameters... It's because you're skipping over the root and will be a guaranteed lack of penetration... a CWI would fail you because he's not going to waste his time continuing... the only time you might get away with this is vertical up or a hot pass tig on pipe (walking the cup)

[@sania9709]

استمررررررر

[@gambiarraprofissional5599]

Kkkkkkkkk

[@josegeraldopereira3385]

Esqueci de pôr a máscara queimei minha vista vendo essa solda!🤣🤣🤣 brincadeira ficou show parabéns

[@RC-Heli835]

Love how sturdy that nozzle looks on that gun.

[@manarhanna5750]

كل الاحترام للعمل الفيديو بس انا زلمة لحيم اول مرة بشوف اللحام من فوق لتحت على حديد خميل

[@bloodybillanderson9294]

Shame on anyone doing downward welds they are never as strong as upward verticle welds and they arent permitted on railcars in the U.S

[@jamesashby9065]

Funny looking railcar

[@magicman_metal_fab]

Worked in a metal shop as an iron worker. It’s NOT permitted there either.

[@robertblackshear8963]

But they are permitted on coastguard vessels with 6011 on the doorways. And pipe welders do it daily with 6010 roots.

[@miketerry4972]

Your right,any good contractors would show you the gate for downhill welds.

[@kenmillwall1885]

In 45 years of welding I have never had to chip of slag after doing any MIG Welding the gas cover protects the weld pool . I can weld Arc Gas Mig and Tig and a coded welder

[@mate7255]

Yeah and even with flux wire there is no slag

[@lylecallor560]

Have you ever ran dual shield flux core we use that at my shop it cooks in very nice and there is slag but it comes off very easily

[@mate7255]

@@lylecallor560 yeah, not really slag but more like white-yellow dust

[@theuniversalbean9352]

@@mate7255 my man that's self shielded flux core not gas shielded

[@rodneycarter5283]

In your "45 years of welding" you've obviously never ran dual shield 😂😂😂

[@user-nm8jr4bw5k]

Как то странно, что на полуавтоматической сварке шлак

[@uyentv5255]

That is great,hi new dear friend

[@joshuamckenzie1670]

I’m not trying to be a online CWI but bud you need to go up…vertically

[@robertblackshear8963]

A good welder can weld downhand. 28 years shipyard experience xrays whole nine yards. It depends on the situation more than anything else.

[@manarhanna5750]

My also i think tha same

[@patriziosergiacomi2153]

Bravo, mo vojo vedè che se magnamo una volta che se so' m'parati de saldà... l' occhi.? Scherzo 🤣🤣🤣🤣.... ottimo insegnamento di come dev'essere veramente una saldatura. Grande.!!

[@gavinchandler3660]

Try and do it vertical up then ill be impressed its easy stuff your doing sorry mate

[@chadmoyer1453]

What is the difference between vertical up and down? I use a miller 145 d/c smaw for maintenance at trucking terminals and use MR 7018 1/8 rods and vertical up seems messy compared to vertical down. Thank you.

[@gavinchandler3660]

@@chadmoyer1453 vertical up welding is more structural welding and coded welding the grain structure of a vertical up weld is more ductility and flex therefore can take more stresses and strain down hand the grain structure is more solid and weaker also i can vertical up and over head weld with MMA process and still have a neat tidy weld

[@lannyfullerjr6956]

Not mig welding. It's flux core welding. Anyway cool vid

[@charlienewman9824]

Thanks for sharing its great that welding brings us all together! Keep up the great work

[@a.adam.1153]

Ну ну, повернули деталь в удобное положение, и давай сверху вниз гнать... с таким подходом любой ПТУ'шник покажет красоту на визуал контроле Про обработку детали я вообще молчу...

[@Kosach72]

Это горе учителя. Смех ещё кого-то учит позорник.

[@jaroslawrhein6831]

Чего разнылись. Покажите как нужно, а не кудахтать.

[@ZZTOP414]

@@jaroslawrhein6831 даже ребенок сможет варить полуавтоматом 😅 это самый простейший вид сварки...

[@patrickfarley8036]

Wow! Kids, this IS NOT the video to watch to learn how to weld! Forget EVERYTHING you just saw! Find a video made by a certified welder with an AWS or Equivalent by country, credibility! Stay away from everyone else until you know right from wrong. Not every non certified welder is a bad welder, But ALL certified welders are good welders!

[@rerikm]

It would be useful if you could point out the issues here in this video.

[@robertblackshear8963]

Oh no their not. There are different classes of welders. I was first class at the shipyard I worked to. You would be shocked at just how bad many certified welders are. And you weld the doorways on some coastguard vessels 6011 downhand. 28 years experienced production welder mig, dualshield fluxcore ceramic backing and of course stick welding.

[@kendraspencer5703]

Beautiful(In my Pharrell voice😁)

[@kimuseni]

This is the best welding tutorial video I have seen

[@nucks4life11]

You havent seen too many then hey?

[@pipefabmadeeasy]

Check out something new kzbin.info/www/bejne/o4Wmf52gnd5sq5Y

[@jaimelopez3229]

You need to use nozzle dip to prevent the build up on your nozzle

[@jasoncampbell8797]

Or paint marker

[@user-lk7rd6sb9m]

Молодцы, шов увидел поменялось мнен.))я домашний сварщик.Мостак👍

[@dhdhhxjhdh1533]

جزاكم الله كل خير

[@camiongrumercedesrachid5861]

شكرا

[@smokerise]

Flux core welds are almost always ran uphill. In America, that is a no no...js. When we run downhill welds it's always with solid wire.

[@austin3626]

Wtf is the big deal with downhill flux core?

[@smokerise]

@@austin3626 any structural design forbids downhill welding for a reason. Penatration is the reason. You get much less in downhill welds. All structural codes require uphill...as in bridges, buildings, anything that flies, rolls, or floats...get it?

[@austingarcia4521]

I been to welding school and I have welded alittle but I could be wrong but that look more 6g 45angle or maybe plate is 4g ether way didnt look vertical and I was always told never run down the only thing that runs down is shit always weld up

[@89giamp]

I want to see this guy work with steel 0.3 cm thin. Whit big plate everybody are professional welder 😂

[@ChefKustom]

Indeed...😆

[@weldmachine]

Thinner material in my experience is easier to weld not harder.

[@ChefKustom]

@@weldmachine please make a video sir..tq

[@weldmachine]

@@ChefKustom Yes can do. Just need some time to fit in between jobs. Very busy in my shop at the moment. If you are serious can let you know after i have posted the video. 👍

[@ChefKustom]

@@weldmachine no worries sir,just take ur time...no worries..😉

[@Gersela.channel]

Terima kasih ilmu nya👍👍👍

[@andreypio9627]

Почему все показывают на толстом металле? Покажите как красиво сварить уставшего японца)) стыковку кузовную, где между слоями гермет, оцинковочку 0,8..и все это без маски, а по звуку, углу наклона и пониманию, как у тебя проволока выходит из сопла.. Красиво варить тоже надо уметь, но это уже чисто для себя или для определенных работ..

[@marco1950-s2b]

Prima di insegnare devi imparare 🤗

[@user-yv8do8nm6h]

수직용접 위에서 아래로해도 되긴하는군요 아래서 위로 하는것보단 밥이 좀 덜차긴하네요

[@michaelhumphrey2476]

Looks like I saw some undercut..

[@wonderful_cat]

Tutorial yang sangat bermanfaat sekali,izin untuk membagikannya,,

[@ovidiojunior4840]

Muito bom excelente dica 👏🏽👏🏽👏🏽👏🏽

[@KhanKhan-sx4ve]

Very nice this video excellent#khanbiharguru

[@user-uu9si8fo9v]

Это ручной сварки шов, а показал как водит на проволоке

[@eugeniosalas9350]

Bueno ustedes lo piden!! Yo en realidad nunca me a gustado soldar prefiero mandar a soldar Pero cuando nó quieren trabajar LO TENGO QUE HACER ÝÓ ES QUE ME GUSTA VERLOS TRABAJAR. PERO COBRAR YÓ.

[@billmoore1936]

To do this welding needs quite a bit of training to get the bee right and the speed right also the wire feed which takes time

[@technicalskillstraining]

Gooood👌👌👌👍

[@johnk9762]

Mig welding doesn't leave a flux. That is either flux core or inner shield, not mig.

[@mahpiulutasioux]

This isn't MIG. flux-cores wire

[@BadarseBreakout]

Yerp cos he's doing it outside you would hear the gas like a cyclone to get a good weld

[@austinlane5533]

Innersheild is flux core isn't it? If I'm not mistaken, all the flux wire I've ever ran through my machine is Innersheild.

[@robertblackshear8963]

@@austinlane5533 Yes. It's the same. Some manufacturers call them by either of the two.

[@betmen7542]

откуда такой толстый навар полуавтоматом , ещё и шлак оббивают. сварка полуавтоматом в углекислотной среде не шлакует 😁😂🤣

[@Uriy7408]

Порошковая проволока,без защитного газа.есть такая опция на полуавтомате а сварщик неделю назад увидел полуавтомат швы ужасные.видать первый раз получилось без раковин.

[@betmen7542]

@@Uriy7408 точно а я думаю чё там шипит , оказывается это порошок с балона туда дует 😁😂🤣 и проволка обмеднёная 😁😂🤣, а оббивают посмотри чем , не сварочной проволкой порошеовой😁😂🤣

[@wongtoby887]

Good job

[@edwingil3040]

Hasta donde se la soldadura mig no deja rastros de carbon es limpia?????

[@GM-ry7gv]

Entonces no sabes nada, porque sé utiliza alambre tubular, o sea que tiene revestimiento interno. La única soldadura que no produce escorias es el GTAW.

[@silvestregonzalez1898]

Esa soldadura que uso es FCAW, la soldadura mig GMAW, deja una mínima de escoria camarada,ilustrate..

[@johnnyggarza2329]

This is NOT GMAW aka Mig... this process is FCAW aka FLUX CORE welding.

[@azouzboulouafa3939]

Ktfham bi ghlat ya akhi

[@MulyasugaraWeldingexperimen]

Good job bro.... 💪💪💪💪

[@weldingtechnologytechnical4820]

Nice video Welding

[@iron9844]

أحسنت

[@user-gr9vj9nc5w]

А как с глубиной провара или это просто заполнение

[@TV-io1cb]

GooD

[@user-gz1ul7in4o]

Ещё один проход на убывания и будет шов выпуклым, огонь.

[@uellingtonsoares2189]

Top

[@jeffhanson9821]

Never ever pull mig .always push

[@danielbeaird6264]

You only pull a mig downhill. Your arc should be leading the puddle in the root... if you push downhill, it's likely your arc is in the puddle and not hitting the root

[@bimokonstruksibaja]

Siip.salam seniman api🙏👍

[@mikesmith-lr8ec]

They must be using flux core wire that will leave slag behind.. probably can't afford shielding gas

[@tangguhekaw4966]

Bukannya malah lebih mudah jika pengelasan dari bawah ke atas? Lebih cepat dan lebih bagus hasinya

[@AbdulHadi-gu3vc]

Mybe this person dont have experient how to welding..

[@luisorlandomunogonzale5736]

Son grandes maestro

[@akhileshchauhan8755]

Fantastic mig velding

[@nucks4life11]

Its not mig. Its flux core

[@iron9844]

good job

[@theuniversalbean9352]

This is FCAW for future reference

[@natas0733]

Nope. Dual shield

[@theuniversalbean9352]

My man dual shield is fcaw

[@natas0733]

@@theuniversalbean9352well you and i know that, but being specific is key when correcting someone. You could have also said it is arc welding and i said no its fcaw. And you coulda said my man fcaw is arc welding

[@theuniversalbean9352]

@@natas0733I suppose but all I was correcting was the process. This is not gmaw, it's fcaw. That's all I wanted to correct. You couldve added on that it's dual shield but it is not incorrect to call it fcaw

[@natas0733]

@@theuniversalbean9352 agreed

[@bintangkarya]

Sempurna

[@gokulcs3010]

3g position the work piece will be vertical and welding methord is starting point down side of the work piece

[@lafusoni4720]

Goodluck

[@quy1981vlog1]

ok đấy bạn

[@bengkelaro3380]

Good job 👍

[@chriscox5568]

You shouldn't run your weave downhill. Run it uphill. And it would've been better if you weren't going to V-up your plates on your horizontal weld to at least grind a groove to get really good penatration.

[@albertomorancasado7216]

Soldadura más fuerte siempre para arriba

[@jossweaver2982]

Never drag hard wire. Mig wire is ment to be pushed. AWS D1.1 will explain. That is a fail!

[@naturalstones9898]

Fluxcore welding

[@enoque5480]

Da pra melhorar ficou bastante mordeduras

[@ronaldoleopoldo4723]

Só soldador da nasa

[@wallacereginaldo2318]

Não façam solda descendente para não serem demitidos

[@chanelkuini5883]

Mantap

[@fiveangels6699]

Amperes and volt not balanced..ive been a welder in ship bldg.and structural since 17 yrs old to 60 yrs old and teach the real positions im also a q.c.supervised steel ship fitter welder .wood builder. and strustural fabricator installations

[@chaseheather3053]

Thats algood to no .ive worked with alot of people that say amount of years experience and what they can do,but wen it comes to actual structual welding/fabricating they suck.trying to show them things have changed over the years but you no u cant teach old dogs new trick

[@user-sv9no9wb1u]

الله ينور

[@gastonemmanuelromero2773]

Con mig no hace falta esa costura

[@mauriziogiasan4411]

top

[@joscarm7319]

Si éste tipo de soldadura Mig tiene que desplazarse de a favor del gas inerte. Francamente No entiendo soldar en descendente y en contra del gas.

[@weldingbilgin]

Süpersin 😳🇹🇷🇦🇿🇵🇰

[@user-jh3xr7vn9p]

Купите балон с газом при таком опыте его вам не хватает работа будет легче

[@kengTUBE]

👍👍👍

[@zonatumana]

👍

[@inspektur9090]

Nice, thanks for the video 👍

[@bassididembele7749]

Très bonne leçon

[@FAUZIAKBAR89]

Saya mau tau..cara bikin vidio vlog ny pakai camera apa bro..?🤝👍🇮🇩🇮🇩🇮🇩

[@robertblackshear8963]

Yep. On point.

[@ahmetdemirali1visvetotojen421]

Shlaka Zavarivanje ovo

[@user-kb3zf3rj1b]

Super 👍

[@antonioneto9613]

Ele está usando arame tubolar alma metal por isso está dando casca este arame alma metal e especial para material enferrujado da mais penetração.

[@ahmetdemirali1visvetotojen421]

SUPPERR

[@user-bs9kg6gk8u]

Почему он показывает вертикал сверху вниз, это правильно для полуавтомата? Прост не в курсе, не варил им.

[@user-uz5fz9qp5d]

Я так понимаю что сварка металла производится порошковой самозащитной проволокой?

[@GM-ry7gv]

Ese movimiento sé llama zigzag o Angulo variable. Se utiliza en todos los procesos de soldadura cambiando (En algunos la velocidad de avance)

[@silvestregonzalez1898]

Camarada,ese proceso que uso se llama FCAW flux core arc welding,,y nos es mig como lo describe,antes de opinar por favor ilustrence...

[@inakirubalcabacoyote7201]

@@silvestregonzalez1898 Es mierda de hilo animado eso es una guarrada,sumado a que suelda en descendente tenemos un cordon sin apenas penetración y falta de fusion,por muy chulo que os parezca que a quedao.

[@negrochileno506]

@@silvestregonzalez1898 gracias por su comentario , ¡ El ataque esta demas !

[@aldochavez301]

This is dual shield welding? Or something like that

[@evpover1897]

IIS Genova check not bad weld you Need more learning