Dye Penetration and Visual Inspection Techniques

Here's a little lesson in how weld testing is done so you can be prepared before the CWI gets onto the jobsite.
Amazon links to tools we used in this video:
- CANTESCO Dye Penetrant Kit: amzn.to/2Y73Byp
- V-WAC Gage: amzn.to/2XSYk22
- Bridge Cam: amzn.to/2XZ0ygs
- Fillet Gages: amzn.to/2Y9Jsre
- Weld Reinforcement Gage: amzn.to/2SAsHoi
VISIT OUR WEBSITE: www.weld.com
FOLLOW US ON INSTAGRAM: / welddotcom
JOIN THE FACEBOOK GROUP - / welddotcom
Talk with Bob, Jason and Mancub!
------------------------------------------------
EQUIPMENT WE LIKE AND USE IN THE SHOP:
CANTESCO ANTI SPATTER SPRAY: cantesco.net/en/home/
WEILER ABRASIVES: weilercorp.com
SELECT ARC WIRE: www.select-arc.com
PFERD ABRASIVES: www.pferdusa.com
ESAB POWER SOURCES: www.ESAB.com
EVERLAST POWER SOURCES: www.everlastgenerators.com
AHP POWER SOURCES: www.ahp.com
TAB AND SLOT WELDING TABLES: www.tabandslot.com
VIDEO SCHEDULE:
MONDAY @ 5:30 PM ET
WEDNESDAY @ 5:30 PM ET
FRIDAY @ 5:30 PM ET
Weld.com is a dedicated to helping you build your career as a welder / fabricator. Whether you’re a hobbyist, student or active in the trade; we are here to help further your craft. If you want to keep learning and interacting with us, make sure you hit that subscribe and notify (bell) button. Join us in the comment section after each video. If you have questions on projects or tests you’re doing now, head over to the Facebook group so you can share pictures with us and get feedback from the community.
FACEBOOK GROUP - / welddotcom
#welddotcom #helpmewelddotcom
Disclaimer: Weld.com is compensated for providing links in our descriptions. However, we only work with companies that we use ourselves and can honestly and ethically recommend to our audience.

[@Welddotcom]

Tell us what you think will be shown in the Dye Pen Test Here to win a bucket dipper...

[@chrisdoeg5199]

I think we will see a crack in plate b with the test.

[@jimtortorelli5032]

Cracks

[@macnudd]

A

[@mrpaint055]

Plate A

[@LextechLighting]

B

[@connecteddj8820]

As a level 2 NDT Inspector in PT and RT this is a great window for any welder that is interested in the inspection process

[@midwestduckslayer5896]

Not to be off subject.. but sending prayers from st louis for bob for what ever he is dealing with!

[@toolbox-gua]

If I don’t learn with You (or Bob M.) its because I don’t want. You guys are fenomenal teachers.

[@GodslilRedneck23]

Eduardo Rosales A thank you sir. We appreciate the feedback.

[@garyborchert61]

I used this penatrant on hydraulic oil pressure tank builds for Queensland power station, very effective and a must use to ensure a no leak unit was built , great content love ya work !😀👌

[@mamannan1423]

Thanks for your clear explain about DPI and instruments usage.

[@ToddLarsen]

I was at the edge of my seat waiting to learn how that test works! I'm also thinking "it's got to be difficult to make a bad weld on purpose" after seeing the copper wire it all made sense. Thanks for sharing and as always keep building👍

[@wadewittman8510]

Plate B is the stuck 🐷! Great video Captain Red Beard!

[@cjbiggar240]

B plate is gonna be the one with the Defect in it 👌 ... thanks for all the great content

[@dicelabiblia7461]

Fantastic video, great teachers in this channel. Thank you

[@nikodimaleshkin7689]

Good technic. Thank you for the given knowledge.

[@user-km5nx2kq4t]

thanks for your excellent tests

[@mystertyie]

Great video took a lot away from today's episode thank you

[@tjvanderloop1686]

Jason Becker is an Awesome AWS Welding Instructor & Visual Welding Inspector. His training is outstanding for any beginner, or professional welder, you will learn from his video-training. Thanks Jason; T J (Tom) Vanderloop, AWS & SME Member, Author and Shop-Instructor

[@michaelcoriglianol7197]

B I can see undercutd in it. Good stuff used the die in a pipe shop i worked in.

[@mortezatuzandehjani4833]

You're Awesome!! This is Perfect and informative video!

[@morraderi]

Great video. Thanks for sharing. Greetings from Brazil!

[@ypaulbrown]

Thanks friends.... great stuff

[@miguelangelsimonfernandez5498]

A very old timer technique used in Spain was chalk and a non greasy solvent like alcohol. Some used gasoline, but that would leave contaminants

[@keithmccullum7929]

Great Teacher thank you

[@mohammedtroy4296]

u.s. marine thank you for your service

[@samcarpenter9424]

Great vid man. im in New Orleans taking my test saturday. what do you suggest i study if i dont cut the mayo?

[@klaus111]

Hey guys, greetings from Germany. A few points I'd like to add: Spraying the dye penetrant can result in a big mess, especially with windows / doors opened. Depending on the length of the weld I prefer spraying in a "bottle" and using a brush to apply. A thin coating is more than enough. Most penetrants are made for temperatures from 5 to 50°C, the cooler it is, the longer it should sit. From 5°C (20-25 mins) to 50°C (5 mins). Also cracks and other "shit" you want to check for have to be open to the surface, that includes being free from dust and other stuff, therefor it's wise to use the cleaner in 90° directly on the weld, to hopefully clean everything. Will you show magnetic particle testing aswell?

[@mathewdavis-adventuresandd6643]

Thank you for that demonstration as I didn't know what a dye test was. I just watch a video of a sailing vessel that lost their rigging costing them thousands of dollars. A dye penetration test could have exposed the shackle that was about to fail if they had taken the time to do the dye test.

[@jasonpope8586]

Super informative as usual.1 question. Can you use strong backs on all D1.1 tests?

[@proteusaugustus]

Top notch 👍🏻🇺🇸

[@henryholliday1]

piece b was my guess and I see some blue coloring in the base metal that gave me a gut feeling that was the bad piece

[@hummingbirdlogisticsinc6762]

Per the navspecsea welding code do the copper coating have to be removed from the welding wire to not produce crackes.

[@JonDingle]

Piece A looks to have some discoloration in the weld beads and also surface deposits that are way different to piece B. Piece A beads look less uniform and more ridged up too. So in my opinion Piece A ang my second choice is Piece B just in case I got it wrong first time!

[@SteveMahdits]

B cracks and craters X-ray would reveal lack of fusion as well most likely visual would reject as well was d17.1 can be very strict on discoloration

[@user-lj4wm4sb8f]

Funny intro! Nice!

[@wayne-oo]

A great demo , but messy and time consuming ! You should do this demo with MPI and see how much faster this can be done !

[@monkipooman]

Can you do a cut and etch, or a bend test on the bad plate? Keen to see what the cooper does to it

[@leebarnhart9725]

"I hate it when people expect results." 😀 Won't effect this old dog but, as always, learned a lot and enjoyed I much.

[@literallyfat5761]

Piece A has the copper in it. You can slightly see the coppery color on the surface.

[@olgajoachimosmundsen4647]

How do you check for cracks on things that don't have a backside, or that which has one that you cannot reach?

[@greggpartridge6288]

Can you use those strongbacks on tests? I didnt think we could. Im in Ontario

[@dan-xl4mg]

i think its piece b cus i believe the filling was tough to full because of the extra material but at the same time it could be a cus its filled a lot more so it could be both but im going for b

[@vodwills]

Wel(d) explained!

[@weldingtechnologytechnical4820]

Very nice Vedeo Technical

[@alessiogabrielebilanzola932]

usefull!!!

[@mexi9787]

B & that’s a cool test I’ve never seen one done till now thank you 🙏🏽🙌🏽💯

[@ypaulbrown]

Slag coldlap with some slag entrapment near surface

[@rtkville]

I sure miss Bob and would like to see him back

[@chrisbookhamer5346]

Cracks in plate B, maybe some porosity under the surface

[@keithmccullum7929]

I wish you showed the MT VT UT RT

[@rafatrill]

Idk but I'm guess A, pretty kool tools thanks I'm get me some

[@powerstroke0459]

I've had aluminum and steel coffer dams pass 15 psi pressure tests but fail dye pen test 2 days later after the dye sets in😰😰

[@michaelbradley1347]

Crack(s) plate B possibly small surface porosity only open to surface.

[@markfryer9880]

Good video. Just one comment. You shouldn't just throw those testing tools in your tool box. They cost good money and are designed for accuracy so at the very least store them in some sort of protective case so they can do the job properly.

[@chrisplayz253]

Good

[@jeremywatterson9594]

In my opinion I would say either lack of fusion or porosity

[@guntern2004]

Liquid Penetrant is used for cracks.

[@SnipeP3]

I use my calibrated eyes 😎👀

[@clevelandgrant4241]

Plate B

[@sinanali3646]

PT TEST indication show undercut, cracks, scarchs, cap porosity, salg inclusions

[@williamlinkenhoger396]

Slag inclusions arent always open to the surface. I dont think I would add that one to the list. Scratches dont count either. Those would be false indications.

[@ypaulbrown]

Don't squeeze the Charmin while cleaning.....gives new meaning to the term Red Beard

[@annaconda8951]

☺️❤️

[@stanwooddave9758]

Your "Bevel" (@ 24:10 of the video) gauge measures both Metric & Imperial, not Metric & Standard.

[@sbaisden100]

Stanwood Dave I call them “Freedom Units” ... ‘Merica :o)

[@gilbertreyna3838]

My guess is piece B

[@macnudd]

What about mag flux inspection?

[@macnudd]

On the failed piece.

[@iainscott616]

B it has at least one crack that I can see.

[@supergerbal909]

I would say cracks and porosity

[@albertoaguirre6290]

It must Be sample B Must!

[@austinclonts7129]

Cracking

[@ChrisAWare]

Any idea if this penatrant can be used on hydraulic cylinders? We have a couple manufacturers of cylinders we know are notorious for welds cracking. We can't test them before rebuilding without risking contamination of our test system. This stuff could save us a lot of time if it will still work with hydraulic oil present.

[@GodslilRedneck23]

ChrisAWare it should work no problem, just have to make sure you use the cleaner on it first. It’s not an expensive setup. It would be worth a shot if you could avoid having to do repairs if you don’t have to.

[@alfredoalonso728]

Good shit what’s up with the boy bob ???

[@willsmith9057]

In a pinch take apart a Sharpie permanent marker n squeeze the ink tube onto the weld let dry then quickly wipe 1-2 times with acetone rag n it'll highlight the crack.

[@cody2254]

A Looks funny. Lets see if I am right or wrong lol

[@kirkreed2705]

What happened to Bob M. And Mr. TIG ?

[@Welddotcom]

Bob is taking some time to deal with some personal matters. Mr TIG hasn't made videos for years.

[@ypaulbrown]

Hope he gets back soon... you two are great together.... Happy birthday Bob....

[@gregoryk.9815]

It's time for your safety write up ( no safety glasses in the shop.)

[@skratdedeu2455]

Its gotta be B I dont trust that two pass cap

[@samgillilan215]

Looks like a crack in plate B. This copper probably isn’t solid copper. Probably has 25% tin content or bronze or brass in it which if it does has zinc in it and definently is what will cause a crack

[@danielbrown7231]

Cracks in plate with two beads.

[@austinchampion4847]

B lack of fusion

[@tracycurtright2671]

The process is much neater ir you spray the penetrant in a cup and put it on with an acid brush. An aircraft mechanic trick.

[@patrickcassidy7008]

# 2

[@beaugodwin7306]

Paused at 1:35, B has the crack, u can c it running down the middle of the 2 beads for a few inches

[@lsellclumanetsolarenergyll5071]

Piece B you can see the void already

[@jameskauffman8405]

Plate "A"

[@leonardanderson3386]

I see comment from 3 weeks ago but my guess is B

[@melgross]

Interesting you used copper. I use ESAB MiG wire. The ones I use don’t have a copper coating. The data sheet extols that, saying that there’s no copper contamination. But, they have wire with copper coatings. So, what gives?

[@GodslilRedneck23]

Mel Gross the copper coating on the wire is so thin it burns off. It’s their to protect the wire from rusting some companies heat treat their solid wire to prevent it from rusting.

[@melgross]

Jason Becker I agree with that, and it’s what I’m sure is true. But then, why would they mention copper contamination?

[@campatterson1358]

Cracks in both!! Lol. No I say crack on B..

[@mitchstephen5491]

Weld A

[@roarkm.o.banjonjeffries3713]

Crack hills that was in the '90s it's a whole new game

[@andypeard1731]

Guessing piece a

[@jeremiahmosier6978]

I think that it is a

[@jeffstevens5983]

I guess A

[@cracken223]

This is ambiguous as in my company after red dye,we let it settle for 12 mins & after white we pause for 5 mins... U aaying it 10 & 10... Tho I'd like to mention i m talking about GI & MS pipes not copper ones

[@Eden_Maker]

🤣🤣🤣🤣🤣

[@johnnavarro539]

I guess b

[@kevsowell]

i guess A

[@alecknowski3450]

B

[@crashbandit3018]

A surface crack.

[@motoxjim929]

Plate b inclusions

[@MRSTEEL-fd7eg]

What happened to Bob? Stop beating around the Bush! Tell the subscribers......

[@Welddotcom]

No beating around the bush going on. When we know more, you guys will know more.

[@Wirewelding]

A

[@Bike-Breakers]

Plate B will fail i think..

[@RickAShriver]

Wow! Gloves and no glass's Ha! Ha! Ha! just taken notes!!!!!!

[@guitarplayer5932]

you never spray cleaner directly onto the part, cleaner obliterates penetrant you dont want it in any cracks