How to coat the base helmet with resin.

[@大野直史-k1p]

造形ベースで同じことをやってます。 いつも参考になります。

[@yuta2010able]

物凄く参考になります。

[@cameronjsmith7382]

This is perfect!!!!!! Great video Pigtail!

[@swegmoney6475]

Thank you for the tutorial! Would you recommend doing this process before proceeding with the details of a sentai helmet? Or should this step come after the details have been added?

[@myheromedia-verse]

Thank you for the tutorial!!!

[@gameofsvart9755]

ギャバン楽しみにしていまーす^_^

[@蛙楓の趣味悠々]

すいません 一つお聞きしたいのですが この作業って何の意味があるのですか？ FRPを使えない環境の代替え方法ですか？

[@PigtailChannel]

その通りです。FRPはガラス繊維を使ったりしますし、海外では入手が難しい場合もありますので、樹脂を使った方法を公開しました。

[@tranminhhieu6880]

Thank you so much !!!!

[@QuanaloaloTOPUAXELIENQUAN]

Great!!

[@SUNSHINE-t-m]

If i were to do this for a full design, should i coat it once assembled? or should i coat the pieces separate and then assemble?

[@SUNSHINE-t-m]

how can i make a mask trhat splits with the coating?

[@PigtailChannel]

To coat the helmet, I try to coat it after it's assembled.

[@rogue2631]

EX-CASTの後処理はどのようにしていますか。また、余ったら戻しても大丈夫ですか。

[@PigtailChannel]

一度容器から出した液を戻すのはお勧めしません。一度容器からあけた液体は水分を含んでしまうので戻さない方が良いです。水分を含むと発泡してしまいます。余ったものは、２液を混ぜて固まったらゴミに出してます。

[@kuronekowatchi]

ベースのウレタンボードは白色より黒色の方が利点があるんでしょうか？ ヘルメット制作に黒いウレタンボードを使っている方が多い気がしたので気になりました

[@PigtailChannel]

ウレタンボードは、どの色を使っても同じように作ることが出来ます。白いウレタンだと引いた線が撮影時にボヤけて映るので、黒いウレタンに白い線を引いて撮影するようになりました。

[@kuronekowatchi]

@@PigtailChannel ありがとうございます！

[@kuronekowatchi]

@@PigtailChannel ありがとうございます！

[@ひらいたかひさ-w4u]

ベースマスクの材料はジョイントマットでしたっけ？ ジョイントマットは柔らかい素材ですが、コーティングした樹脂にヒビ割れはしないのでしょうか。

[@PigtailChannel]

樹脂でコーティングしても、力が加わる場所はヒビが入ります。また、高いところから落としたりしても割れたりします。思っていたよりは強度は無いです。表面をキレイにすることが目的なら有効と思います。

[@ひらいたかひさ-w4u]

@@PigtailChannel 様　ご返信ありがとうございます。マスク製作に役立てたいと思います。

[@Hey_Stune]

Hello I was wondering what was the yellow thing that you mix with the polyester and what is the b liquid (I think it's the durcissor but unsure).

[@PigtailChannel]

The resin I used is the type that hardens when A and B are mixed. I think the B component is the hardener. Usually, A and B are sold as a set.

[@Hey_Stune]

Thanks !

[@ここに居たのねとりぱいちゃん]

このマスクの重さはどれくらいでしょうか？

[@PigtailChannel]

計ってみたところ、コーティング無しだと145g、コーティング有りだと400gでした。

[@ancientthundercast]

I know you always thank me for my comments i have done before but I get the idea what you use for the helmet designs for the pieces to put on for Kamen Rider helmet pieces for including super sentai I’m the same one who went by the name of RangerHypeReviews I changed one part of my name to Rider from Hype and that design you use for the parts of the helmets are kind of like what I work out on like a workout mat has the same material to the Lego shaped mat you use

[@avyannee7739]

Hello what does it mean Letter size?

[@PigtailChannel]

Letter size is the size of the paper. In Japan, where I live, A4 size copy paper is mainly used, but in America and other countries, letter size copy paper seems to be used.

[@avyannee7739]

@@PigtailChannel thank you. In Europe, austria A4 size the copy paper too😊

[@村滝邦典]

張り子でも通用します？

[@PigtailChannel]

実はワタクシも張り子で作ることを考えていました。海外の視聴者様の中にはスポンジシートを入手できない方もいらっしゃるので、新聞紙で代用できないかと考えています。今度、張り子の要領で作ってみます。

[@diegovallejos3986]

Kamen rider evol kobra helmet

[@pratinodarma1951]

it is stil get cracked?

[@PigtailChannel]

I checked the base helmet I made at that time, but it didn't have any cracks.

[@pratinodarma1951]

@@PigtailChannel it nice if not cracked. Because eva foam easily bend

[@pratinodarma1951]

@@PigtailChannel what ratio resin A and B? 1:1? and what ratio with talc?

[@PigtailChannel]

@@pratinodarma1951 The ratio of resin varies depending on the resin used, so please read the instruction manual for the resin. Mix talc so that the resin does not drip. There is no fixed weight.

[@pratinodarma1951]

@@PigtailChannel thankyou very much for your info & tutorial. Maybe in another time i will ask you again :)