6G Mig/Flux Pipe Welding

[@weldtube]

👇WeldTube Store👇 www.weldlife.com

[@ShadowMaster_6]

what happen to him?

[@ALVERGAZ0]

Brother… thanks a million. I have always welded structure always been scared of taking a pipe test. I got a job offer paying 32 dlls an hour so I was watching this video the night before the test. And well you know the rest.. I’m buying some welding caps right now and some FR shirts cause I start Monday. The video helped out brother thanks

[@jarrodmartin2204]

Wish this dude was still on this show, awesome welder 👨‍🏭

[@ShadowMaster_6]

What happen to him they never said what happen

[@jarrodmartin2204]

Bro I’d love to know that too

[@CR-nn1by]

@@jarrodmartin2204he went to go work somewhere, that’s why he left weldtube but he was the best instructor there hands down

[@slickricc2079]

They don’t get paid enough

[@zenteno5p]

For me i follow this guy long time i like the way he explain all the time👌

[@stevemcfadden6180]

Well you just got a fan4life. I've been welding forever 25 years it's been awhile since I ran Mig and flux core filling cap. I've got a fantastic job opportunity this Friday without your video I don't think I would have made it just been so long I kind of forgot. Incredibly professionally done you do a fantastic job thank you thank you thank you and keep up the good work young man you're doing fantastic!!!!!

[@catabaticanabatic3800]

Don't put yourself down. If it passes inspection /test, it IS perfect. Nice work buddy.

[@donsal.t.1765]

If it holds and nobody gets hurt AND you get paid it's all good or perfect lol

[@raulvizcaino8191]

This video just landed me a 28$. Thanks weld tube! Great job guys!

[@brandonhernandez9260]

Raul Vizcaino was it the same test? 6” schedule 80 pipe?

[@elias1579]

LoL I have a test next week for this at the same wage.

[@georgeguerra4615]

Are they hiring right now

[@jonnyboy7628]

Congrats! 🎈

[@joshuawaldon5669]

Same test coming up Friday for the same rate of pay

[@Kingturbo86]

These videos help a lot hadn’t run wire in 6 years not a clue what to set the machine at for my test today. Watched this video the night before and passed the next day

[@ctbegayiii8479]

Just watching your videos helps me learn new techniques in Stick/Flux-core/ Mig. I work as a Structural welder out the field & in the fab-shop, Great videos. Keep up the gd job bro.

[@caseynabors6235]

Excellent welding! Flux core is fast but will never look as good as old school 7018!

[@bernalherrera1066]

Thanks you are the best instructors starting to begging and end so you are the one again continue your blog don't stop it

[@michaelmartinezsantos5174]

I am a gtaw smaw welder in some plants here in saudi arabia with special metal,,i just weld fcaw and mig in plates but when i watched you YOUR THE BEST, GMAW + FCAW IS THE HARDEST TO DO IN PIPES but YOU DID IT WITH EASE.. HIGH SALUTE TO YOU SIR I LEARNED A LOT FROM YOU AND ON YOUR CHANNEL..KEEP IT UP MORE POWER SIR.. GOD BLESS

[@joshhhuuaa9167]

Thanks man so much now I can study this video and use my Lincoln machine at home and practice for the job down the street thanks again!

[@krs1732]

Never mind I saw it at the other side.

[@enriquegutierrez597]

Best 6g mig and flux video online. Thank you very much for making it.👍👍💯💯💰💰

[@OzieLombok]

Nice and smooth welding,,, big applaus from Indonesia

[@justinhall8318]

Now yall can disagree with me, but in my opinion and opinions of the old guys who taught me all my welding skills, I'd NEVER do circles with a fluxcored wire, due to the chance of slag inclusions. I'd do a weave but stay on the front edge of the puddle but not circles where you come back into the puddle.

[@daskiier]

Justin Hall as long as you’re not over exaggerating and are keeping the with the puddle any movement you do with fluxcore will be fine as the slag stays molten

[@txdocprich_8404]

Cory Knowles - Yep as long as that puddle is hot and wet you’ll be fine. Little tiny circles to get coverage is fine.

[@KosmischPeacock]

yeah, that's what I was taught too, a slight weave on uphill, a bit like: (|(|(|(|(|(|(|(|(| - with "(" passing the tip of its arch over "|"

[@Nunezkta]

Like he said “Personal preference”

[@jeffgreer198613]

Yea you couldn't step far but as long as that puddles tight you can get away with alot. I do shell sections on rotary kilns. It's all 100% x-ray.

[@charliwright1128]

Great video! This really helped my students to see what the puddle should look like as its burning into the root.

[@santanavazquez9272]

Thanks!

[@aldeanbilly2696]

Great job! Thanks again and keep up the amazing work and information.

[@don0234]

Great demo. The right info and no extra bs. Well done

[@ofwwelder8622]

My coming tradetest is 6gr mig im nervous but when i see this video i feel so confident thanks for your tips and technics

[@bobmoffatt4133]

Very nice lesson Hjalmar.

[@bobmoffatt4133]

I get to use this in my class today. Thanks for the content. Strong lessons.

[@boodrow24m]

Just tested $28/hr. Passed! Thanks for the video!

[@The940don]

do you have to switch over the wire when you switch to flux

[@rws0010]

Very nice brother, I’ve been waiting to see this one!

[@rafaelsolano2358]

That boy Pedro’s hood 🔥

[@henrybresyn9204]

Good video thanks these are getting me through Tulsa Welding School because I am definitely not getting the help I need there

[@CodyKowalskiBladesmith]

Henry Bresyn I went to the same school man and I agree the place is pretty trash

[@avant-gardemarmalade7605]

Same thing here bud 🤠

[@MrNoe713]

Was that suck back on the bottom right side of the root?

[@irvingarcia215]

“Burn learn and eventually will earn !” 🔥🔥🔥🔥

[@stearnbros]

Honour to have watched this video very good tutorial you have a good way of explaining in detail the process of mig I thoroughly enjoyed watching it nice one bro you definitely no how to lay that metal down

[@mikemyars9267]

I have a weld test Friday Feb 8 2019. 6g position weld 2 inch 160 wall. I have only use a postioner when using this process. Can I walk to cup in a position weld like you would with a positioner? ? Please help. I have no way of practicing before the test

[@daniel_cx1423]

I noticed you did your root 1/4 of the pipe at a time is it the same with fill and cap or is it 1/2 the pipe

[@mdsafwaanullah6796]

So very strong & very well excellent welding brother I m your big fan

[@darkforcex7362]

i love the zero g videos. although you have made lots, please continue to video the open face welds. i do love 3/32 landings tho

[@kforkitchenlover7662]

Its awesome.. As a new lerner its halp a lot...Thanks dude.

[@stearlingestes4213]

Thanks for sharing. From SW Missouri.

[@randynelson9773]

.045” 7100 esab dual shield flux wire? Gas shielded. Some of the prettiest solid flat beads one can lay down.

[@robertcampos4204]

Thats smell of mig & flex, peace feeling

[@nathangonzalez2334]

I never grind the root pass before I lay down the flux.

[@kenharrelson3673]

Ran this test today but on 4in sch 40 I found it pretty hard but that’s probably because I’ve been running duelshield on structural for the last five years not much pipe but I was feeling like Superman because I ran a 2in sch 40 aluminum then stainless then carbon all in GTAW and bent out went to the mig and set the gap at a 1/8 in wit the 3/32 root face

[@darlinharahap5235]

Brother, in the future, you will tell me what the fire and wire speed are, most of the welder can only operate it, but you don't necessarily know about wire speed, thank you please

[@jameswilliams__337]

Definitely a fan of your videos. I'm looking for a very well explained video on RMD,, I figured u can help me out with that

[@rodrigobalcazar9079]

Felicitaciones por este material y a la vez agradecerte por estos vídeos que son de mucha ayuda para los que seguimos este arte tan bello como es el tema de la soldadura.Lo sgte , seria de gran ayuda para tus seguidores que estamos suscritos a tu canal que tus vídeos pudieran ser subtitulados al español ya que por este lado de Sudamérica (Calama ,Chile )lado Norte de este largo y bello País soy un fiel seguidor de tu pericia en este tema de soldadura. Lo otro para este pass room que (cordon de raiz)que amps utilizas ?y para el relleno ascendente al igual que el remate ? Y por último que tipo que de mezcla, y tipo de alambre utilizas? Se despide atte Rodrigo Balcázar Michea. Que Dios te bendiga y gracias por recibir est sugerencia .Byeee

[@UniteForgetLeftRight]

Wish I had access to this video 7 years ago for a weld test. Nobody had ever asked me to do a root pass with a wire fed process before and it was 6gR.

[@dalefuller5507]

That ring really will mess with you got to be on your game to pass that one

[@littlepochita21]

Well done , i ll learned a lot in this vid 😎😎

[@aaronm3091]

Would be good to note the wire size, i assume you’re using 0.35 based on your settings, 0.45 seems to be what companies are using more often. Settings would be a lot different in that case

[@denigrator6399]

Was there a cool down period? I’ve been running .072 self shield on structural and you really can’t lay beads back to back

[@vinayagamvedha9138]

Hi sir , thanks 👍 ,I get idieya how to weld about 6G Poisson's, wire speed and voltage ,root pass and capping ,I have one dwout sir,root pass use that wire speed 195 ok, voltage 17.5, it's ok ,than hotpass useing wire speed 300 and voltage 25,same voltage 25 and wire speed 300 using capping sir?

[@tristanburns82]

@weldtube have you tested out one of them Lincoln STT migs?

[@darkforcex7362]

i have these guns on my bench, but i need practice. thanks so much for the video.

[@wildchild1161]

For the mill 252 , what voltage would you use for a fill pass /w .035 wire .( just use the 17.5 @ 195ish for the hole thing or would you change it ?) 6" sch80 pipe . what would be a good gap size between the 2 pipes

[@joons3374]

this was exactly what I was looking for... I got a new job but never did Root pass or flux wire D:

[@ernestoaquinodocumentary4384]

Sir i have a question the downhill on mig is that the standard welding procedure ?or there is also uphill position welding procedure?

[@daveosland3199]

Esab wire- Dual shield I presume. 75/25 gas? Thanks!

[@leslieobregon8540]

Excuse me, how much voltage would you give in the root with gmaw in ascending ?, and how much voltage does it give to the filling and finishing in fcaw?

[@ak471911able]

@@weldtube what wire thickness are you running on both mig and fluxcore?

[@jamessonger3]

Was the reg mig wire 045 as well? Think i missed that if u said it.

[@MrJj1620]

should 035 hard wire

[@ttsupra87]

14:52 isn't that cold wire in the right??

[@christanmenia5868]

Nice work buddy😍😍😍😍😍😍

[@michaelj6645]

What type of gas are you running if any with hardwire mig? What size wire?(.035/.045)

[@donsal.t.1765]

You ever do .045 mug? What is it supposed to sounds like?

[@stephenandroschuk8011]

Would this technique be fairly similar for running roots with RMD? I have a pipeline test at the end of next week and i have really never ran wire since school lol. They are giving me 4 days of booth time to get it on lock.

[@andrewsheed8746]

I could be wrong but I believe RMD root is hardwire just like he used

[@stevelafrance32]

Could you use this setting for 3/32 gap and I/16 of land in horizontal

[@ronaldhorca8532]

What is voltage/wire speed settings in capping?

[@slickricc2079]

25 v & 300 ws

[@brandonlee9476]

Great welds and love the decals on the hood, reppin the good Lord is the only way to go!

[@krs1732]

How would you do the root if the pipe was already tacked with a bigger gap like 3/16 and had no root face? I tried dragging but it's hard and you tend to get whiskers. Plus, do you have any tips on how to tie in on a pipe like that?

[@gonzaloaceves373]

@@krs1732 no need to turn the heat down when you see the key hole getting big stop for a second and before the puddle cool down pull the triger and do couple of c's and and repeat the same thing over until youre able to controll with out stopping

[@RudyRex]

Nice tutorial as always bro. Wanted to ask if you could do one on a square butt joint with a gap. 3g/4g half inch carbon with 6011 5/32 root and cap with 7018 1/8 uphill if possible. It's for a test i got coming up at shipyard but I can't seem to find tutorials on it

[@ックエリ-j1y]

I heard something similar. Job was hiring like 140 stick welders, test was 3g WITH NO BEVEL

[@keatenpues1461]

How many fillers did you do and what was ur settings for the cap

[@tray8411]

Just found your vid,, for beginners like me that's great instruction as you lay a bead..Thank you

[@miguelwelder8113]

5:15 17.5 volts 195ws👍

[@НаильВалеев-щ1ф]

утянуло на потолке, провалился корешок, да и облицовка не очень, но спасибо за видео, информативно...)

[@JoseSanchez-nq1fb]

Hi, brother, I like them. all your videos, I would like to know if it is possible to make the root pass with fluxcored, thank you

[@georgiojansen7758]

was waiting for this👍

[@georgiojansen7758]

@@trmn8trx131 what do you mean

[@georgiojansen7758]

@@trmn8trx131 ok

[@DVANTJKR]

My company does a 6G with a restrictor. All mig .045 Lincoln wire

[@DVANTJKR]

Any tips

[@abrahamdavila9318]

Does the mig root and flux root run the same?

[@dg8511]

Why did you do root pass top to down and not from bottom to top?

[@darcypatterson1600]

Hey bro do yall sale pipe coupons if so how can i get some thanks and keep the videos coming love them

[@jessedarcourt4164]

Hey man I love the videos I’m a big fan of all your work. But I’m in need of you doing a video on a penetration 6gr flux core test, bevel to flat pipe.

[@commietube4273]

This dude is sharp!

[@kuldeepsinghsingh1961]

Good welding.

[@dranrebracan8006]

I want to see is the uphill welding not downhill weld...

[@thomasmcnicholas8656]

You say MIG process for the bead pass....... are you short circuiting or RMD ???

[@anatedesco2489]

Hello had a question about the setting is it the same for 5 inch heavy wall

[@raymondjolly9230]

I see your land was 3/32 what was your gap on the 6",thanks.

[@kyvenmarquis7258]

That's not on the 0.045"/1.2mm wire?

[@paulaecheverry6159]

excelente tu video,pero no dejas ver el amperaje ni voltaje de la maquina para saber como graduar la maquina saludos soy un fiel seguidor de colombia

[@TomFromYoutube]

Could you do a flux core root or is that a bad idea?

[@bangtorus6962]

how about your ampere n voltage in capping pass bro???pls tell me

[@horastampuboloon9889]

thanks for the study, I want to learn welding, but money is the barrier. can you teach me the advantages of welding. I am in Indonesia

[@rubenmeza3326]

Nice video bro

[@aarongonzalezreyes2159]

Aya en Estados Unidos cuánto vale un curso de soldadura??

[@howietoney8687]

could you do a video on 6g 12 inch pipe with 7010 hyp rod with single bead puddle cap...

[@crashbandit3018]

Where did you get that sweet weld cap brother? Awesome videos too keep me coming. #gostros!!

[@MrNoe713]

Ryan Allison Axbry weld caps in Baytown Tx

[@crashbandit3018]

Awesome. I work in Pasadena. It’s right down the road. I’m very interested in getting one.

[@MrNoe713]

Ryan Allison look for them on offer up

[@ralph1618]

Have a $32 a hour test 2inch schedule 80, never welded with mig/fluxcore on pipe before but im hoping this is enough. Will update

[@metalfab2449]

U never updated bro how'd it go

[@ralph1618]

@@metalfab2449 it went good! Still currently working with them thanks for asking!!

[@metalfab2449]

Sweet that means they're treating you right lol

[@jhunelucas4157]

Good. Weld sir keep up the good work

[@urickalexander5057]

Thank you I have test for a job on this it was helpful

[@milbertmanzano962]

Is it possible to do uphill in this 6g position?

[@omfaudji8353]

Hiii...how many amperes to root

[@oscarramirez1065]

Muy bien gracias por enseñar..thanks for teaching

[@jamwantytiwari2680]

🙏⚘🥀🌹🌺very good i learn you vidio u such a great

[@kenharrelson3673]

Needless to say I didn’t get the penetration needed to support the hot pass blew threw the root on the hard side went back in and did a repair on the root with the hard wire then hot passed filled her up and capped her out ended up popping a strap on the repair gonna try again Monday with a little bit bigger gap see what happens

[@petergreen8269]

No rollers?? Always best to keep the gun at the top and spin the pipe instead right??? Gravity sucks haha

[@juanonalvarezcadereytanuev8438]

Wirespeed? And volt?

[@C150sn]

juanon De cadereyta nuevo León yo también ando batallando para regular la máquina 🤣🤨 no dicen cuánto

[@eltoxico2977]

Si dijo we, 25v y 300 de alambre flux...y la mig 19.5v y 195 en el alambre

[@ak471911able]

@@eltoxico2977 mig 17.5v 195 wire speed( velocidad del alambre) lo que no dijo fue el grosor del alambre, puede ser .045 o .035